Features of TOKO Brand Flux Cored Welding Wire AWS A5.29 E81T1-K2C
Superior welding performance for high-strength steel applications
High Tensile Strength Deposits
- Designed to deposit metal with high tensile strength
- Suitable for welding high-strength steels
- Tensile strength range: 550-690 MPa or higher
Excellent Welding Performance
- Stable arc for smooth and consistent welds
- Suitable for all-position welding
- Versatile for various welding applications
Gas Shielding
- Used with CO2 or argon/CO2 mixture
- Protects weld pool from atmospheric contamination
- Minimizes porosity and welding defects
Low Spatter & Easy Slag Removal
- Low levels of spatter for easier cleaning
- Slag is easily removable
- Neat and clean weld appearance
Mechanical Properties
- Good ductility and toughness
- Withstands intended service conditions
- Meets or exceeds industry standards
Certifications & Diameter Availability
- Certified by AWS and other standards bodies
- Available in various diameters (1.2mm, 1.6mm, etc.)
- Complies with regional and national standards
Technical Specifications
| Property | Value | Standard |
|---|---|---|
| Tensile Strength | 550-690 MPa (min) | AWS A5.29 |
| Yield Strength | 460 MPa (min) | AWS A5.29 |
| Elongation | 22% (min) | AWS A5.29 |
| Impact Toughness | 27J at -29°C | AWS A5.29 |
| Shielding Gas | CO2 or Ar/CO2 mix | - |
| Positions | All positions | - |
The information contained or otherwise referenced herein is presented only as "typical" without guarantee or warranty, and TOKO Corporation expressly disclaims any liability incurred from any reliance thereon. Typical data and Test results for mechanical properties, deposit or electrode composition and other properties were obtained from a weld produced and tested according to prescribed standards, and should not be assumed to be the expected results in a particular application or weldment. Actual results will vary depending on many factors, including, but not limited to, weld procedure, plate chemistry and temperature, weldment design and fabrication methods. Users are cautioned to confirm by qualification testing, or other appropriate means, the suitability of any welding consumable and procedure before use in the intended application.